- EN 14700 alloy category: ISO 1071: E C NiCu-B
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8.20 g/cc
- View Details →
- EN 14700 alloy category: Ni3
- Available forms: Atomized powders (Fuseweld - Powder welding)
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 56 - 63 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 7.80 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: -120° C up to +400° C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C FeC - GF 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ti, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 350 HB (as welded) approx. 54 HRC (one layer on cast iron)
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 12
- Available forms: welding electrodes
- Major alloying elements: C, Si, Cr, Ni, Mn, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: -
- Service temperature: -120 °C up to +350 °C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: - 20° C up to +300° C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 190 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: From room temperature up to + 1200° C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 190 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C Ni-CI 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 160 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →