Cold wear
Date (default)
Cold wear
- Buffer layers - Build up - Cladding - Joining
- Cast iron
- Dissimilar & stainless steels
- Manganese steel
- Metal-to-Earth wear
- High impact, high abrasion
- High stress, high abrasion
- Overalloyed solutions
- Severe abrasion
- Severe abrasion with corrosion
- Severe abrasion with erosion
- Severe abrasion with erosion, temperature
- Severe impact
- Metal-to-Metal wear
- Hot wear (tool steel)
- Hot wear with corrosion & thermal fatigue
- Superalloy Hardfacing
- Cobalt base superalloys
- Iron base superalloys
- Nickel base superalloys
- Tungsten carbide base superalloys
Available forms
Hardness
Major hard-phase(s)
Suitability - Abrasion
Suitability - Corrosion
Suitability - Erosion
Suitability - Impact
Suitability - Temperature
- EN 14700 alloy category: EN 14700 E Z Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, V, Fe
- Major hard-phase(s): Martensite
- Hardness as per DIN 32525-4: 57 - 61 HRC
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, Fe
- Major hard-phase(s): Martensite
- Hardness as per DIN 32525-4: 55 - 60 HRC
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, V, Fe
- Major hard-phase(s): Martensite
- Hardness as per DIN 32525-4: 55 - 60 HRC
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, V, W, Fe
- Major hard-phase(s): Martensite
- Hardness as per DIN 32525-4: 50 - 55 HRC
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 7
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Mn, Ni, Cr, Mo, Fe
- Major hard-phase(s): Martensite
- Hardness as per DIN 32525-4: 38 - 40 HRC
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →