- EN 14700 alloy category: Fe 15
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, B, Fe
- Major hard-phase(s): Chromium carbides, Niobium carbides
- Hardness as per DIN 32525-4: 62 - 66 HRC
- Service temperature: 450 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Ni3
- Available forms: Bare rods, cored wires, atomized powders
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 56 - 63 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 7.80 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes, cored wires
- Major alloying elements: C ,Si, Cr, Ni, Mn, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 14
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Mn, Mo, Ni, Cr, V, Nb, B, Fe
- Major hard-phase(s): Chromium carbide, complex carbides
- Hardness as per DIN 32525-4: 62 - 66 HRC
- Service temperature: 600 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 20
- Available forms: Welding electrodes
- Major alloying elements: Spherical Fused Tungsten Carbides, Fe matrix
- Major hard-phase(s): Spherical Fused Tungsten Carbides
- Hardness as per DIN 32525-4: 60 - 66 HRC / 700 - 865 HV
- Service temperature: 500 C
- Weld deposit density: ~ 13.10 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiCu-B
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8.20 g/cc
- View Details →
- EN 14700 alloy category: Fe 13
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, V, B, Fe
- Major hard-phase(s): Iron carbide, Chromium carbide
- Hardness as per DIN 32525-4: 61 - 65 HRC
- Service temperature: 500 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 16 gtz
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, W, Nb, B, Fe
- Major hard-phase(s): Metallic carbo-borides
- Hardness as per DIN 32525-4: 65 - 70 HRC / 800 - 1050 HV
- Service temperature: 500 C
- Weld deposit density: ~ 8.20 g/cc
- View Details →
- EN 14700 alloy category: Fe 7
- Available forms: welding electrodes
- Major alloying elements: C, Si, Cr, Ni, Mn, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 410 HB
- Service temperature: up to 450 C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 15
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Cr, Ni, Mo, V, W, B, Fe
- Major hard-phase(s): Chromium carbide, complex carbides
- Hardness as per DIN 32525-4: 60 - 65 HRC
- Service temperature: 480 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Ni3
- Available forms: Atomized powders (Fuseweld - Powder welding)
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 56 - 63 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 7.80 g/cc
- View Details →
- EN 14700 alloy category: AWS A5.11: ENiCrFe-2 / mod.
- Available forms: welding electrodes
- Major alloying elements: C, Mn, Cr, Mo, Nb, Fe, Ni
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: -196 °C up to 550 °C
- Weld deposit density: ~ 8 g/cc
- View Details →