- EN 14700 alloy category: AWS A5.11: ENiCrFe-2 / mod.
- Available forms: welding electrodes
- Major alloying elements: C, Mn, Cr, Mo, Nb, Fe, Ni
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: -196 °C up to 550 °C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: AWS A5.11: ENiCrFe-3
- Available forms: welding electrodes
- Major alloying elements: C, Mn, Cr, Mo, Nb, Fe, Ni
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: -269 °C up to above 550 °C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes, cored wires
- Major alloying elements: C ,Si, Cr, Ni, Mn, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes, cored wires
- Major alloying elements: C ,Si, Cr, Ni, Mn, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes, cored wires
- Major alloying elements: C ,Si, Cr, Ni, Mn, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C ,Si, Cr, Ni, Mn, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: 300 C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiCu-B
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8.20 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: From room temperature up to + 1200° C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: - 20° C up to +300° C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: Fe 11
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: 180 - 200 HB (as welded) 330 - 370 HB (work hardened)
- Service temperature: - 60° C up to +300° C
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C Ni-CI 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C Ni-CI 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 160 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →