- EN 14700 alloy category: Z Fe 16
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Mn, Cr, Nb, W, Fe
- Major hard-phase(s): Chromium carbide, Niobium carbide, Tungsten carbide
- Hardness as per DIN 32525-4: 65 - 70 HRC
- Service temperature: 450 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 6
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, B, Fe
- Major hard-phase(s): Iron carbide, chromium carbide
- Hardness as per DIN 32525-4: 58 - 63 HRC
- Service temperature: 350 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 13
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, V, B, Fe
- Major hard-phase(s): Iron carbide, Chromium carbide
- Hardness as per DIN 32525-4: 61 - 65 HRC
- Service temperature: 500 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Z Fe 16
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Mn, Cr, Mo, Nb, W, Fe
- Major hard-phase(s): Chromium carbide, Niobium carbide, Tungsten carbide
- Hardness as per DIN 32525-4: 65 - 70 HRC
- Service temperature: 550 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Z Fe 14
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 50 - 55 HRC
- Service temperature: 350 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Z Fe 14
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, V, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 58 - 62 HRC
- Service temperature: 400 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Z Fe 14
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Ni, Mo, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 50 - 55 HRC
- Service temperature: 350 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 15
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, B, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 56 - 62 HRC
- Service temperature: 350 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 15
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 58 - 63 HRc
- Service temperature: 350 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: EN 14700 E Fe 15
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Cr, B, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 60 - 64 HRc
- Service temperature: 400 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 15
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Mo, Others++, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 60 - 64 HRC
- Service temperature: 450 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
- EN 14700 alloy category: Fe 14
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Mo, Ni, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 42 - 44 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →