Nickel base superalloys
Date (default)
Nickel base superalloys
- Buffer layers - Build up - Cladding - Joining
- Cast iron
- Dissimilar & stainless steels
- Manganese steel
- Metal-to-Earth wear
- High impact, high abrasion
- High stress, high abrasion
- Overalloyed solutions
- Severe abrasion
- Severe abrasion with corrosion
- Severe abrasion with erosion
- Severe abrasion with erosion, temperature
- Severe impact
- Metal-to-Metal wear
- Cold wear
- Hot wear (tool steel)
- Hot wear with corrosion & thermal fatigue
- Superalloy Hardfacing
- Cobalt base superalloys
- Iron base superalloys
- Tungsten carbide base superalloys
Available forms
Hardness
Major hard-phase(s)
Suitability - Abrasion
Suitability - Corrosion
Suitability - Erosion
Suitability - Impact
Suitability - Temperature
- EN 14700 alloy category: Ni3
- Available forms: Atomized powders (Fuseweld - Powder welding)
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 56 - 63 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 7.80 g/cc
- View Details →
- EN 14700 alloy category: Ni3
- Available forms: Bare rods, cored wires, atomized powders
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 56 - 63 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 7.80 g/cc
- View Details →
- EN 14700 alloy category: Ni3
- Available forms: Atomized powders (Fuseweld - Powder welding)
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 39 - 43 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 8.20 g/cc
- View Details →
-
- EN 14700 alloy category: Ni3
- Available forms: Bare rods, cored wires, atomized powders
- Major alloying elements: C, Cr, B, Si, Fe, Ni
- Major hard-phase(s): Fine metallic borides
- Hardness as per DIN 32525-4: 35 - 40 HRC
- Service temperature: 650 C
- Weld deposit density: ~ 8.20 g/cc
- View Details →