- Home
- Main Catalog
- Superalloy Hardfacing
- Iron base superalloys
Iron base superalloys
Date (default)
Iron base superalloys
- Buffer layers - Build up - Cladding - Joining
- Cast iron
- Dissimilar & stainless steels
- Manganese steel
- Metal-to-Earth wear
- High impact, high abrasion
- High stress, high abrasion
- Overalloyed solutions
- Severe abrasion
- Severe abrasion with corrosion
- Severe abrasion with erosion
- Severe abrasion with erosion, temperature
- Severe impact
- Metal-to-Metal wear
- Cold wear
- Hot wear (tool steel)
- Hot wear with corrosion & thermal fatigue
- Superalloy Hardfacing
- Cobalt base superalloys
- Nickel base superalloys
- Tungsten carbide base superalloys
Available forms
Hardness
Major hard-phase(s)
Suitability - Abrasion
Suitability - Corrosion
Suitability - Erosion
Suitability - Impact
Suitability - Temperature
- EN 14700 alloy category: Fe 16 gtz
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Nb, Mo, W, B, Fe
- Major hard-phase(s): Metallic carbo-borides
- Hardness as per DIN 32525-4: 69 - 72 HRC / 1000 - 1200 HV
- Service temperature: 900 C
- Weld deposit density: ~ 8.60 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 16 gtz
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Nb, Mo, W, B, Fe
- Major hard-phase(s): Metallic carbo-borides
- Hardness as per DIN 32525-4: 69 - 72 HRC / 1000 - 1200 HV
- Service temperature: 900 C
- Weld deposit density: ~ 8.50 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 16 gtz
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Nb, Mo, B, Fe
- Major hard-phase(s): Metallic carbo-borides
- Hardness as per DIN 32525-4: 67 - 72 HRC / 900 - 1200 HV
- Service temperature: 850 C
- Weld deposit density: ~ 7.6 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 16 gtz
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, W, Nb, B, Fe
- Major hard-phase(s): Metallic carbo-borides
- Hardness as per DIN 32525-4: 65 - 70 HRC / 800 - 1050 HV
- Service temperature: 500 C
- Weld deposit density: ~ 8.20 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 16 gtz
- Available forms: welding electrodes, cored wires, composite wearplates
- Major alloying elements: C, Si, Mn, Cr, Nb, B, Fe
- Major hard-phase(s): Metallic carbo-borides
- Hardness as per DIN 32525-4: 66 - 69 HRC / 850 - 1000 HV
- Service temperature: 700 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →