High stress, high abrasion
Date (default)
High stress, high abrasion
- Buffer layers - Build up - Cladding - Joining
- Cast iron
- Dissimilar & stainless steels
- Manganese steel
- Metal-to-Earth wear
- High impact, high abrasion
- Overalloyed solutions
- Severe abrasion
- Severe abrasion with corrosion
- Severe abrasion with erosion
- Severe abrasion with erosion, temperature
- Severe impact
- Metal-to-Metal wear
- Cold wear
- Hot wear (tool steel)
- Hot wear with corrosion & thermal fatigue
- Superalloy Hardfacing
- Cobalt base superalloys
- Iron base superalloys
- Nickel base superalloys
- Tungsten carbide base superalloys
Available forms
Hardness
Major hard-phase(s)
Suitability - Abrasion
Suitability - Corrosion
Suitability - Erosion
Suitability - Impact
Suitability - Temperature
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, Fe
- Major hard-phase(s): Chromium carbide
- Hardness as per DIN 32525-4: 40- 50 HRC (first layer) 50 - 55 HRC (pure weld deposit)
- Service temperature: 450 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Nb, W, B, Fe
- Major hard-phase(s): Niobium carbides
- Hardness as per DIN 32525-4: 52 - 57 HRC (first layer) 55 - 60 HRC (pure weld deposit)
- Service temperature: 550 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, Nb, V, W, Fe
- Major hard-phase(s): Niobium carbides
- Hardness as per DIN 32525-4: 45 - 50 HRC (first layer) 54 - 58 HRC (pure weld deposit)
- Service temperature: 600 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →
-
- EN 14700 alloy category: Fe 8
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Cr, Mo, Ti, Fe
- Major hard-phase(s): titanium carbide
- Hardness as per DIN 32525-4: 45 - 50 HRC (first layer) 54 - 58 HRC (pure weld deposit)
- Service temperature: 500 C
- Weld deposit density: ~ 8.00 g/cc
- View Details →