Cast iron
Date (default)
Cast iron
- Buffer layers - Build up - Cladding - Joining
- Dissimilar & stainless steels
- Manganese steel
- Metal-to-Earth wear
- High impact, high abrasion
- High stress, high abrasion
- Overalloyed solutions
- Severe abrasion
- Severe abrasion with corrosion
- Severe abrasion with erosion
- Severe abrasion with erosion, temperature
- Severe impact
- Metal-to-Metal wear
- Cold wear
- Hot wear (tool steel)
- Hot wear with corrosion & thermal fatigue
- Superalloy Hardfacing
- Cobalt base superalloys
- Iron base superalloys
- Nickel base superalloys
- Tungsten carbide base superalloys
Available forms
Hardness
Major hard-phase(s)
Suitability - Abrasion
Suitability - Corrosion
Suitability - Erosion
Suitability - Impact
Suitability - Temperature
- EN 14700 alloy category: ISO 1071: E C NiCu-B
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8.20 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C Ni-CI 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C Ni-CI 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 160 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C Ni-CI 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 160 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 190 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 190 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes, cored wires
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C NiFe-1 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ni, Cu, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 170 HB
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →
-
- EN 14700 alloy category: ISO 1071: E C FeC - GF 1
- Available forms: welding electrodes
- Major alloying elements: C, Si, Mn, Ti, Fe
- Major hard-phase(s): -
- Hardness as per DIN 32525-4: approx. 350 HB (as welded) approx. 54 HRC (one layer on cast iron)
- Service temperature: -
- Weld deposit density: ~ 8 g/cc
- View Details →